日本无机Nipponmuki超高温绝缘布BCM-430/650/665/665AD Super high temperature insulation Siliglass Siligalss is high silicate heat resistant fiberglass consisted of SiO2 by 96% or more and can be used for long hours under high temperature of 1,000°C or higher. It is excellent in thermal durability, chemical stability and electrical insulation properties. Characteristics Asbestos Free Fireproof Resists Thermal Shock Resists Chemicals Electrical Resistivity Minimal Shrinkage Resists Molten Steel Non-Hazardous Cost Effective Good Workability Applications High temperature thermal insulation and absorption material Welding & Burning Protection Drop Cloth, Welding Curtains, Furnace Curtain, Heat Treat & Stress Relief Insulation High temperature filter media Filter media for hot gases and chemicals. High temperature structural materials Rocket nose cones, etc. Wicks of oil heater Catalytic carrier for oxidation-reduction reaction Catalytic carrier of deodorization equipment. Treating material for organic solution gas. Others Electric cable insulator for hair driers. High temperature buffers and seals. Cloth Standard specification Product Code Thickness (mm) Width (mm) Length (m) Weight (g/m2) Product Tensile Strength (N/25mm) Tensile Strength After Heating (N/25mm) Heat Shrinkage (%) Weave Warp Weft Warp Weft BCM-430 0.40 525 100 270 >78 >78 >29 >29 196 >127 >137 >88 294 >137 >196 >98 490 >294 >196 >98 343 >196 >196 >98 392 >245 >343 >196 735 >490 >343 >196 882 >637 >343 >196 <7.0 Satin Heat shrinkage : Percentage of length reduction with 1100°C applied for 30 minutes. (BCS-665 is with 1200°C applied for 30 minutes) Tensile strength after heating : Retension of tensile strength after 30 minutes heating at 1100°C. (BCS-665 is after 30 minutes heating at 1200°C) BCS-665U,BCS-665AD,BCS-12U and BCS-12 are JIS A 1323(flame resisting examination)passing goods.